抗磨白口鑄鐵的化學成分
|
牌號 |
C |
Si≤ |
Mn≤ |
P≤ |
S≤ |
CR |
Ni |
Mo≤ |
其他 |
|
Kmtbni4cr2-DT |
2.4-3.0 |
0.8 |
2.0 |
0.15 |
0.15 |
1.5-3.0 |
3.3-5.0 |
1.0 |
|
|
KMTBNI4CR2-GT |
3.0-3.6 |
0.8 |
2.0 |
0.15 |
0.15 |
1.5-3.0 |
3.3-5.0 |
1.0 |
|
|
KmTBCr9Ni5 |
2.5-3.6 |
2.0 |
2.0 |
0.15 |
0.15 |
7.0-11 |
4.5-7.0 |
1.0 |
|
|
KmTBCr2 |
2.1-3.6 |
1.2 |
2.0 |
0.15 |
0.10 |
1.5-3.0 |
1.0 |
1.0 |
cu≤1.2 |
|
KmTBCr8 |
2.1-3.2 |
1.5-2.2 |
2.0 |
0.10 |
0.03 |
7.0-11.0 |
10 |
1.5 |
cu≤1.2 |
|
KmTBCr12 |
2.0-3.3 |
1.5 |
2.0 |
0.10 |
0.06 |
11.0-14.0 |
2.5 |
3.0 |
cu≤1.2 |
|
KmTBCr15Mo |
2.0-3.0 |
1.2 |
2.0 |
0.10 |
0.06 |
14.0-18.0 |
2.5 |
3.0 |
cu≤1.2 |
|
KmTBCr20Mo |
2.0-3.3 |
1.2 |
2.0 |
0.10 |
0.06 |
18-23.0 |
2.5 |
3.0 |
cu≤1.2 |
|
KmTBCr26 |
2.0-3.3 |
1.2 |
2.0 |
0.10 |
0.06 |
23.0-30.0 |
2.5 |
3.0 |
cu≤2.0 |
抗磨白口鑄鐵的硬度
|
牌號 |
鑄態硬度≥ |
硬化態硬度≥ |
軟化退火態硬度≤ |
|||
|
HRC |
HBW |
HRC |
HBW |
HRC |
HBW |
|
|
Kmtbni4cr2-DT |
53 |
550 |
56 |
600 |
- |
- |
|
KMTBNI4CR2-GT |
53 |
550 |
56 |
600 |
- |
- |
|
KmTBCr9Ni5 |
50 |
500 |
56 |
600 |
- |
- |
|
KmTBCr2 |
46 |
450 |
56 |
600 |
41 |
400 |
|
KmTBCr8 |
46 |
450 |
56 |
600 |
41 |
400 |
|
KmTBCr12 |
46 |
450 |
56 |
600 |
41 |
400 |
|
KmTBCr15Mo |
46 |
450 |
58 |
650 |
41 |
400 |
|
KmTBCr20Mo |
46 |
450 |
58 |
650 |
41 |
400 |
|
KmTBCr26 |
46 |
450 |
56 |
650 |
41 |
400 |
鑄態組織
共晶碳化物M7C3+奧氏體
硬化態組織
共晶碳化物M7C3+二次碳化物+馬氏體+殘留奧氏體
使用特性
有很好的淬透性，有良好的耐蝕性和抗高溫氧化性，適用于較大沖擊載荷的磨料磨損