PP366-3臺(tái)灣福聚 PP 366-3
-
性能項(xiàng)目
|
測(cè)試條件
|
測(cè)試方法
|
數(shù)值/描述
|
單位
|
機(jī)械性能
|
拉伸強(qiáng)度(引張強(qiáng)度)
|
|
ASTM D638/ISO 527
|
35
|
kg/cm²(MPa)[Lb/in2]
|
斷裂伸長(zhǎng)率
|
|
ASTM D638/ISO 527
|
350
|
%
|
拉伸模量
|
|
ASTM D638/ISO 527
|
14500
|
kg/cm²(MPa)[Lb/in2]
|
拉伸屈服伸長(zhǎng)率(延伸率)
|
|
ASTM D638/ISO 527
|
350
|
%
|
拉伸斷裂伸長(zhǎng)率(延伸率)
|
|
ASTM D638/ISO 527
|
350
|
%
|
彎曲模量(彎曲彈性率)
|
|
ASTM D790/ISO 178
|
15000
|
kg/cm²(MPa)[Lb/in2]
|
彎曲強(qiáng)度
|
|
ASTM D790/ISO 178
|
|
kg/cm²(MPa)[Lb/in2]
|
洛氏硬度
|
|
ASTM D785
|
105
|
kg·cm/cm(J/M)ft·lb/in
|
IZOD 缺口沖擊強(qiáng)度
|
1/4" 23℃
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
1/4" -30℃
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
1/8" 23℃
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
1/8" -30℃
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
Charpy沖擊強(qiáng)度
|
23℃ (缺口)
|
ASTM D256/ISO 179
|
5
|
kg·cm/cm(J/M)ft·lb/in
|
-30℃(缺口)
|
ASTM D256/ISO 179
|
2
|
kg·cm/cm(J/M)ft·lb/in
|
23℃(無(wú)缺口)
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
-30℃(無(wú)缺口)
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
物性性能
|
比重(密度)
|
|
ASTM D792/ISO 1183
|
0.9
|
|
成型收縮率
|
|
ASTM D955
|
1.2
|
%
|
熔融指數(shù)(流動(dòng)系數(shù))
|
200℃/5kg
|
ASTM D1238/ISO 1133
|
3
|
g/10min
|
220℃/10kg
|
ASTM D1238/ISO 1133
|
|
g/10min
|
吸水率 23℃/24H
|
|
ASTM D570/ISO 62
|
0.02
|
%
|
熱性能
|
熱變形溫度
|
退火
|
ASTM D648/ISO 75
|
|
℃(℉)
|
未退火
|
ASTM D648/ISO 75
|
|
℃(℉)
|
維卡軟化點(diǎn)
|
|
ASTM D1525/ISO R306
|
|
℃(℉)
|
熔點(diǎn)
|
|
-
|
|
℃(℉)
|
燃燒性(率)
|
|
UL94
|
|
|
線性膨脹系數(shù)
|
|
ASTM D696/ISO 11359
|
|
mm/mm.℃
|