ALCUDIA® EVA PA-539
乙烯醋酸乙烯共聚物
REPSOL
產(chǎn)品說明:
EVA copolymer ALCUDIA® PA-539 is suitable for film extrusion and extrusion coating. This material combines easy processability with excellent mechanical and optical properties. It contains antioxidant additives.
TYPICAL APPLICATIONS
· Film extrusion
· Extrusion coating
Recommended melt temperature below 200°C to avoid the decomposition of the polymer. Processing conditions should be optimised for each production line.
|
|
||||
|
總體 |
|
|||
|
材料狀態(tài) |
|
|||
|
添加劑 |
|
|||
|
特性 |
|
|||
|
用途 |
|
|||
|
機構評級 |
|
|||
|
加工方法 |
|
|||
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|
密度 (73°F) |
0.937 |
g/cm3 |
ISO 1183 |
|
熔流率（熔體流動速率） (190°C/2.16 kg) |
2.0 |
g/10 min |
ISO 1133 |
|
抗環(huán)境應力開裂 (F50) |
> 300 |
hr |
ASTM D1693 |
|
醋酸乙烯含量 |
18.0 |
wt% |
|
|
薄膜 |
額定值 |
單位制 |
測試方法 |
|
薄膜厚度 - 經(jīng)測試 |
2.0 |
mil |
|
|
拉伸應力 |
|
|
ISO 527-3 |
|
MD : 斷裂, 2.0 mil, 吹塑薄膜 |
3770 |
psi |
|
|
TD : 斷裂, 2.0 mil, 吹塑薄膜 |
3190 |
psi |
|
|
伸長率 |
|
|
ISO 527-3 |
|
MD : 斷裂, 2.0 mil, 吹塑薄膜 |
320 |
% |
|
|
TD : 斷裂, 2.0 mil, 吹塑薄膜 |
640 |
% |
|
|
落錘沖擊 (2.0 mil, 吹塑薄膜) |
600 |
g |
ISO 7765-1 |
|
埃爾曼多夫抗撕強度 |
|
|
ISO 6383-2 |
|
MD : 2.0 mil, 吹塑薄膜 |
0.45 |
lbf |
|
|
TD : 2.0 mil, 吹塑薄膜 |
|
|
|