| 牌號 | Type 316不銹鋼絲 | ||||||||
| 美國UNS | S31600 | ||||||||
| 對應標準 | ASTM A580/A580M-2018 | ||||||||
| 不銹鋼絲 | |||||||||
| Stainless Steel Wire | |||||||||
| 歸類 | 奧氏體不銹鋼 | ||||||||
| Type 316 化學元素成分含量(%) | |||||||||
| 成分 | C | Si | Mn | P | S | Cr | Ni | Mo | N |
| 最小值 | - | - | - | - | - | 16 | 10 | 2 | - |
| 最DA值 | 0.08 | 1 | 2 | 0.045 | 0.03 | 18 | 14 | 3 | 0.1 |
| Type 316 機械性能 | |||||||||
| 條件 | 熱處理或狀態 | 抗拉強度 | 屈服點 | 延伸率 | 斷面收縮率 | ||||
| σb | σs | δ | ψ | ||||||
| Mpa | Mpa | % | % | ||||||
| A | 冷精軋 | ≥620 | ≥310 | ≥30 | ≥40 | ||||
| A | 退火 | ≥520 | ≥210 | ≥35 | ≥50 | ||||
| 注:Condition A —— Annealed as a final heat treatment. | |||||||||
| Material in Condition A may be given a final cold drawing for size control or finish, or both, slightly raising tensile strength. |