牌號
|
X2CrNiMoN 17-11-2奧氏體不銹鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
歐標(biāo)鋼號
|
1.4406
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
對應(yīng)標(biāo)準(zhǔn)
|
EN 10088-1-2005
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
不銹鋼 第1部分:不銹鋼的清單
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Staehle Stainless steels. Part 1:List of stainless steels
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
歸類
|
奧氏體不銹鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
性能
|
耐腐蝕
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
標(biāo)簽
|
奧氏體不銹鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
密度
|
8 g/cm3
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
X2CrNiMoN 17-11-2 化學(xué)元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S ?
|
Cr
|
Ni ?
|
Mo
|
N
|
|
|
|
|
|
|
最小值
|
-
|
-
|
-
|
-
|
-
|
16.5
|
10
|
2
|
0.12
|
|
|
|
|
|
|
最DA值
|
0.03
|
1
|
2
|
0.045
|
0.015
|
18.5
|
12.5
|
2.5
|
0.22
|
|
|
|
|
|
|
① 未經(jīng)買方同意，不得隨意向鋼中添加表中未列的元素，冶煉精加工除外。采取一切必要措施以防在廢鋼和生產(chǎn)原料中帶入這些元素，因?yàn)槠鋾魅蹁摰臋C(jī)械性能，降低鋼的適用性。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
? 對于棒材、線材、型材、光亮產(chǎn)品和相關(guān)的半成品，硫含量最大允許 0.030%。特定的硫含量范圍可提高特定的性能。對于將進(jìn)行機(jī)加工的產(chǎn)品，建議硫含量控制在0.015~0.030%范圍內(nèi)。對于要求焊接性能的，建議硫含量控制在 0.008~0.030%范圍內(nèi)。對光亮產(chǎn)品，建議硫含量最DA允許 0.015%。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
? 因?yàn)樘厥庠?，例如用來制作無縫管的不銹鋼其熱加工性要求必需將δ鐵含量降到最DI，或低的導(dǎo)磁率，鎳含量最DA可提高1.00%
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
物理性能
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
各溫度°C時(shí)彈性模量
|
20°C與各溫度間熱膨脹系數(shù)
|
熱導(dǎo)率
|
比熱容
|
電阻率
|
磁性
|
|
20
|
100
|
200
|
300
|
400
|
500
|
100°C
|
200°C
|
300°C
|
400°C
|
500°C
|
20°C
|
20°C
|
20°C
|
|
GPa
|
10-6K-1
|
W/m.K
|
J/kg.K
|
Ω.mm2/m
|
|
200
|
194
|
186
|
179
|
172
|
165
|
16
|
16.5
|
17
|
17.5
|
18
|
15
|
500
|
0.75
|
no*
|
|
*-Small amounts of ferrite and/or martensite caused by cold deformation will increase the magnetizability. (由冷變形產(chǎn)生的少量鐵素體和/或馬氏體將提高磁化率.）
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|