牌號
|
1.4305不銹鋼板和鋼帶
|
|
|
|
|
|
|
|
|
|
|
X8CrNiS18-9
|
|
|
|
|
|
|
|
|
|
對應標準
|
NF EN 10088-2-2005
|
|
|
|
|
|
|
|
|
|
普通用途不銹鋼板和鋼帶的交貨技術條件
|
|
|
|
|
|
|
|
|
|
Part2:Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
|
|
|
|
|
|
|
|
|
|
歸類
|
奧氏體不銹鋼
|
|
|
|
|
|
|
|
|
|
標簽
|
標準等級
|
|
|
|
|
|
|
|
|
|
X8CrNiS18-9 化學元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Cu
|
N
|
|
最小值
|
-
|
-
|
-
|
-
|
0.15
|
17
|
8
|
-
|
-
|
|
最DA值
|
0.1
|
1
|
2
|
0.045
|
0.35
|
19
|
10
|
1
|
0.11
|
|
◎ 未經買方同意，不得隨意向鋼中添加表中未列的元素，冶煉精加工除外。采取一切必要措施以防在廢鋼和生產原料中帶入這些元素，因為其會削弱鋼的機械性能，降低鋼的適用性。
|
|
|
|
|
|
|
|
|
|
|
◎ 在詢價和訂購時可商定更嚴格的碳含量范圍。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
X8CrNiS18-9 機械性能
|
|
|
|
|
|
|
|
|
|
|
條件
|
熱處理或狀態
|
抗拉強度
|
屈服點
|
斷后伸長率或延伸率
|
|
|
|
|
|
|
σb
|
σs
|
δ
|
|
|
|
|
|
|
Mpa
|
Mpa
|
%
|
|
|
|
|
|
|
熱軋中厚板：T ≤ 75mm⑥
|
+AT
|
500~700
|
( t )
|
( t )
|
|
|
|
|
|
|
Rp0.2：≥ 190①③
|
T＜3mm：≥35③④
|
|
|
|
|
|
|
Rp1.0：≥ 230①②
|
T ≥ 3mm：≥35③⑤
|
|
|
|
|
|
|
③
|
|
|
|
|
|
|
|
◎ T-厚度；l-縱向; t-橫向
|
|
|
|
|
|
|
|
|
|
|
◎ +A=軟化退火；+QT=淬火及回火；+P=沉淀硬化；+AT=固溶退火；+SR=消除應力
|
|
|
|
|
|
|
|
|
|
|
① 對于連續熱軋產品，可在詢價和訂購時商定Rp0.2(即表中σs)的最小值提高20MPa，Rp1.0的最小值提高10MPa。
|
|
|
|
|
|
|
|
|
|
|
② 僅作指導
|
|
|
|
|
|
|
|
|
|
|
③ 如果在軋制寬度<300mm的情況下，采用縱向試驗件，最小值減小如下:抗壓強度-15MPa，恒定標距的延伸率-5%，比例標距延伸率-2%。
|
|
|
|
|
|
|
|
|
|
|
④ T＜3mm時適用于標距為80mm、寬度為20mm的試件。也可以使用標距為50mm、寬度為12.5mm的試件。
|
|
|
|
|
|
|
|
|
|
|
⑤ T ≥3mm時適用于標距為5.65√S的試件。
|
|
|
|
|
|
|
|
|
|
|
⑥ T＞75mm，可以協商機械性能。
|
|
|
|
|
|
|
|
|
|
|
* 交貨條件下無抗晶間腐蝕; 致敏條件下無抗晶間腐蝕（根據EN ISO 3651-2進行測試）。
|
|
|
|
|
|
|
|
|
|