牌號
|
X6CrMoNb17-1不銹鋼板和鋼帶
|
|
|
|
|
|
|
|
|
|
|
1.4526
|
|
|
|
|
|
|
|
|
|
對應標準
|
NF EN 10088-2-2005
|
|
|
|
|
|
|
|
|
|
普通用途不銹鋼板和鋼帶的交貨技術條件
|
|
|
|
|
|
|
|
|
|
Part2:Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
|
|
|
|
|
|
|
|
|
|
歸類
|
鐵素體不銹鋼
|
|
|
|
|
|
|
|
|
|
標簽
|
特殊等級
|
|
|
|
|
|
|
|
|
|
X6CrMoNb17-1 化學元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
|
N
|
更多
|
|
最小值
|
-
|
-
|
-
|
-
|
-
|
16
|
0.8
|
-
|
Nb：[7×(C+N)+0.1]~1
|
|
最DA值
|
0.08
|
1
|
1
|
0.04
|
0.015
|
18
|
1.4
|
0.04
|
|
◎ 未經買方同意，不得隨意向鋼中添加表中未列的元素，冶煉精加工除外。采取一切必要措施以防在廢鋼和生產原料中帶入這些元素，因為其會削弱鋼的機械性能，降低鋼的適用性。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
X6CrMoNb17-1 機械性能
|
|
|
|
|
|
|
|
|
|
|
條件
|
熱處理或狀態
|
抗拉強度
|
屈服點
|
斷后伸長率或延伸率
|
|
|
|
|
|
|
σb
|
σs
|
δ
|
|
|
|
|
|
|
Mpa
|
Mpa
|
%
|
|
|
|
|
|
|
冷軋帶鋼：T ≤ 8mm
|
+A
|
480~560
|
l：≥280；t：≥300
|
≥ 25①
|
|
|
|
|
|
|
◎ T-厚度；l-縱向; t-橫向
|
|
|
|
|
|
|
|
|
|
|
◎ +A=軟化退火；+QT=淬火及回火；+P=沉淀硬化；+AT=固溶退火；+SR=消除應力
|
|
|
|
|
|
|
|
|
|
|
① T＜3mm時適用于標距為80mm、寬度為20mm的試件。也可以使用標距為50mm、寬度為12.5mm的試件。T ≥3mm時適用于標距為5.65√S的試件。
|
|
|
|
|
|
|
|
|
|
|
* 交貨條件下有抗晶間腐蝕; 焊接狀態下有抗晶間腐蝕（根據EN ISO 3651-2進行測試）。
|
|
|
|
|
|
|
|
|
|