牌號
|
1.4513壓力容器用不銹鋼扁平
|
|
|
|
|
|
|
|
|
|
|
|
X2CrMoTi17-1
|
|
|
|
|
|
|
|
|
|
|
對應標準
|
NF EN 10028-7-2008
|
|
|
|
|
|
|
|
|
|
|
壓力容器用不銹鋼扁平產品
|
|
|
|
|
|
|
|
|
|
|
Flat products made of steels for pressure purposes - Part 7 : stainless steels
|
|
|
|
|
|
|
|
|
|
|
歸類
|
鐵素體不銹鋼
|
|
|
|
|
|
|
|
|
|
|
X2CrMoTi17-1 化學元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
|
N
|
Ti
|
|
|
ZUI小值
|
-
|
-
|
-
|
-
|
-
|
16
|
0.8
|
-
|
0.3
|
|
|
ZUI大值
|
0.025
|
1
|
1
|
0.04
|
0.015
|
18
|
1.4
|
0.02
|
0.6
|
|
|
◎ 未經買方同意，不得隨意向鋼中添加表中未列的元素，冶煉精加工除外。采取一切必要措施以防在廢鋼和生產原料中帶入這些元素，因為其會削弱鋼的機械性能，降低鋼的適用性。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
X2CrMoTi17-1 機械性能
|
|
|
|
|
|
|
|
|
|
|
|
條件
|
熱處理或狀態
|
抗拉強度
|
屈服點
|
斷后伸長率或延伸率
|
沖擊吸收能量
|
|
|
|
|
|
|
σb
|
σs
|
δ
|
KV2
|
|
|
|
|
|
|
Mpa
|
Mpa
|
%
|
J
|
|
|
|
|
|
|
C：T ≤ 4
|
+A
|
400~550
|
l：≥200；t：≥220
|
23 ①
|
-②
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
◎C- 冷軋帶鋼; H- 熱軋帶鋼; P- 熱軋中厚板；T- 厚度；t- 橫向；l-縱向。
|
|
|
|
|
|
|
|
|
|
|
|
◎+A=軟化退火；+AT=固溶退火；+QT=淬火及回火；+RA=再結晶退火。
|
|
|
|
|
|
|
|
|
|
|
|
*抗晶間腐蝕根據EN ISO 3651-2進行測試。在交貨條件下：有；在焊接狀態下：有。
|
|
|
|
|
|
|
|
|
|
|
|
① T＜3mm：該值適用于標距為80mm、寬度為20mm的試件，也可以使用標距為50mm、寬度為12.5mm的試件。T ≥3mm：該值適用于標距為5.65√S的試件。
|
|
|
|
|
|
|
|
|
|
|
|
② 由于產品最大厚度很小，無法可驗證的值（制備沖擊試驗件的要求適用于:T≥6mm）
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
高溫下的最小屈服強度
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Material designation
|
Heat treatment
|
Minimum 0.2% proof strength Rp0.2,MPa
|
|
condition
|
at a temperature (in°C) of:
|
|
Name
|
Number
|
|
50①
|
100
|
150
|
200
|
250
|
300
|
350
|
400
|
|
X2CrMoTi17-1
|
1.4513
|
+A
|
-
|
250
|
240
|
230
|
220
|
210
|
205
|
200
|