產(chǎn)品 :
|
X1CrNi25-21建筑用耐腐蝕鋼片/板和帶材
|
|
|
|
|
|
|
|
|
編號(hào) :
|
1.4335
|
|
|
|
|
|
|
|
|
分類：
|
奧氏體不銹鋼-特殊等級(jí)
|
|
|
|
|
|
|
|
|
密度:
|
7.9 g/cm 3
|
|
|
|
|
|
|
|
|
標(biāo)準(zhǔn):
|
|
|
|
|
|
|
|
|
|
EN 10088-2:2005不銹鋼。通用耐腐蝕鋼片/板和帶材交貨技術(shù)條件
|
|
|
|
|
|
|
|
|
EN 10028-7:2007壓力用鋼制扁平產(chǎn)品。不銹鋼
|
|
|
|
|
|
|
|
|
EN 10216-5:2014壓力用無縫鋼管。技術(shù)交付條件。不銹鋼管
|
|
|
|
|
|
|
|
|
EN 10253-3:2008對(duì)焊管件。無特殊檢驗(yàn)要求的鍛造奧氏體和奧氏體-鐵素體（雙相）不銹鋼
|
|
|
|
|
|
|
|
|
EN 10253-4:2008對(duì)焊管件。有特殊檢驗(yàn)要求的鍛制奧氏體和奧氏體-鐵素體（雙相）不銹鋼
|
|
|
|
|
|
|
|
|
EN 10297-2:2005機(jī)械和一般工程用無縫圓形鋼管。不銹鋼。技術(shù)交付條件
|
|
|
|
|
|
|
|
|
EN 10088-1:2005不銹鋼。不銹鋼清單
|
|
|
|
|
|
|
|
|
EN 10088-4:2009不銹鋼。建筑用耐腐蝕鋼片/板和帶材交貨技術(shù)條件
|
|
|
|
|
|
|
|
|
Chemical composition % of steel X1CrNi25-21 (1.4335): EN 10088-2-2005
|
|
|
|
|
|
|
|
|
|
Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
|
|
|
|
|
|
|
|
|
|
C
|
Si
|
Mn
|
Ni
|
P
|
S
|
Cr
|
Mo
|
N
|
|
max 0.02
|
max 0.25
|
max 2
|
20 - 22
|
max 0.025
|
max 0.01
|
24 - 26
|
max 0.2
|
max 0.11
|
|
|
|
|
|
|
|
|
|
|
|
Mechanical properties of steel X1CrNi25-21 (1.4335)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (+A)
|
470-670
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (+A)
|
200
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (+AT)
|
180
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
KV - Impact energy (J) transverse, (+A)
|
+20°
|
-196°
|
|
|
|
|
|
|
|
60
|
60
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
KV - Impact energy (J) longitud., (+A)
|
+20°
|
|
|
|
|
|
|
|
|
100
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (+A)
|
40
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (+AT)
|
45
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HB): (+AT)
|
220
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Properties of steel X1CrNi25-21 (1.4335)
|
|
|
|
|
|
|
|
|
|
Resistance to intergranular corrosion: in the delivery condition - yes; in the sensitized condition - yes
|
|
|
|
|
|
|
|
|
|
Steel shal not be applied at a metal temperature lower than -270 ° C
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|