Grade :
|
Z3CN18-10耐腐蝕鋼片/板和帶材
|
|
|
|
|
|
|
|
Number:
|
X2CrNi19-11
|
|
|
|
|
|
|
|
Classification:
|
奧氏體不銹鋼
|
|
|
|
|
|
|
|
Density:
|
7.9 g/cm 3
|
|
|
|
|
|
|
|
Standard:
|
|
|
|
|
|
|
|
|
EN 10088-2:2005不銹鋼。通用耐腐蝕鋼片/板和帶材交貨技術(shù)條件
|
|
|
|
|
|
|
|
EN 10088-3:2005不銹鋼。一般用途耐腐蝕鋼的半成品、棒材、線材、型材和光亮產(chǎn)品的交貨技術(shù)條件
|
|
|
|
|
|
|
|
EN 10028-7:2007壓力用鋼制扁平產(chǎn)品。不銹鋼
|
|
|
|
|
|
|
|
EN 10216-5:2014壓力用無(wú)縫鋼管。技術(shù)交付條件。不銹鋼管
|
|
|
|
|
|
|
|
EN 10217-7:2005壓力用焊接鋼管。不銹鋼管
|
|
|
|
|
|
|
|
EN 10296-2:2005機(jī)械和一般工程用焊接圓鋼管。不銹鋼。技術(shù)交付條件
|
|
|
|
|
|
|
|
EN 10253-4:2008對(duì)焊管件。有特殊檢驗(yàn)要求的鍛制奧氏體和奧氏體-鐵素體（雙相）不銹鋼
|
|
|
|
|
|
|
|
EN 10272:2007壓力用不銹鋼棒
|
|
|
|
|
|
|
|
EN 10263-5:2001冷鐓和冷擠壓用鋼條、棒材和線材。不銹鋼交貨技術(shù)條件
|
|
|
|
|
|
|
|
EN 10250-4:2000一般工程用開(kāi)口鋼模鍛件。不銹鋼
|
|
|
|
|
|
|
|
EN 10297-2:2005機(jī)械和一般工程用無(wú)縫圓形鋼管。不銹鋼。技術(shù)交付條件
|
|
|
|
|
|
|
|
EN 10253-3:2008對(duì)焊管件。無(wú)特殊檢驗(yàn)要求的鍛造奧氏體和奧氏體-鐵素體（雙相）不銹鋼
|
|
|
|
|
|
|
|
EN 10088-1:2005不銹鋼。不銹鋼清單
|
|
|
|
|
|
|
|
EN 10088-5:2009不銹鋼。建筑用耐腐蝕鋼棒材、棒材、線材、型材和光亮產(chǎn)品的交貨技術(shù)條件
|
|
|
|
|
|
|
|
EN 10088-4:2009不銹鋼。建筑用耐腐蝕鋼片/板和帶材交貨技術(shù)條件
|
|
|
|
|
|
|
|
Equivalent grades:
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Chemical composition % of steel X2CrNi19-11 (Z3CN18-10 ): EN 10088-2-2005
|
|
|
|
|
|
|
|
|
特定的硫含量范圍可以改善特定的財(cái)產(chǎn)。對(duì)于可加工性，建議并允許將硫含量控制在0.015%至0.030%之間。對(duì)于可焊性，建議并允許將硫含量控制在0.008%至0.030%之間。對(duì)于可極化性，建議將硫含量控制在最大0.015%。
|
|
|
|
|
|
|
|
|
未經(jīng)買(mǎi)方同意，不得故意將本表中未列出的元素添加到鋼材中，除非對(duì)鑄件進(jìn)行精加工
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
C
|
Si
|
Mn
|
Ni
|
P
|
S
|
Cr
|
N
|
|
max 0.03
|
max 1
|
max 2
|
10月12日
|
max 0.045
|
max 0.015
|
18 - 20
|
max 0.11
|
|
|
|
|
|
|
|
|
|
|
Mechanical properties of steel X2CrNi19-11 (Z3CN18-10 )
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (+A)
|
460-700
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (+AT)
|
460-680
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (+AT+C)
|
740-780
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (+AT)
|
180
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (+A)
|
180-220
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
KV - Impact energy (J) transverse, (+A)
|
+20°
|
-196°
|
|
|
|
|
|
|
60
|
60
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
KV - Impact energy (J) longitud., (+A)
|
+20°
|
|
|
|
|
|
|
|
100
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (+A)
|
35-45
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) longitud., (+AT)
|
40
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Nominal diameter (mm):
|
2 - 50
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Z - Reduction in cross section on fracture (%)
|
63-68
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HB): (+A)
|
215
|
|
|
|
|
|
|
|
Brinell hardness (HB): (+AT)
|
200
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|