| 比重 | 1.41 | ASTM D-792 | |
| 吸收率 (23℃,60%RH) | 0.22 | % | ASTM D-570 |
| 表面電阻率 | 1×10 | Ω | ASTM D-257 |
| 伸縮率 (23℃) | 55 | % | ASTM D-638 |
| 120D沖擊強度 (Notch t3.2mm) | 6.0 | kgf.cm/cm | ASTM D-256 |
| 拉伸沖擊強度 (t3.2mm S type) | 105 | kgf.cm/cm | ASTM D-1822 |
| 斷裂強度 (t2mm) | 560 | kgf.cm/cm | ASTM D-732 |
| 洛氏硬度 | M80 | M scale | ASTM D-785 |
| 曲折彈性率 (23℃) | 2.50 | ×10kgf/cm | ASTM D-790 |
| 拉伸強度 (23℃) | 580 | kgf.cm/cm | ASTM D-638 |
| 彎曲強度 (23℃) | 820 | kgf.cm/cm | ASTM D-790 |
| 耐電壓 | 19 | KV/mm | ASTM D-149 |
| 導電率 (10HZ) | 3.7 | ASTM D-150 | |
| 個質損耗系數 (10HZ) | 0.007 | ASTM D-150 | |
| 體積電阻率 | 1×10 | Ω.cm | ASTM D-257 |
| 燃燒性 (t0.8mm) | HB | UL 94 | |
| 線膨脹系數 (20℃-80℃) | 13 | ×10-5cm/cm/℃ | ASTM D-696 |
| 熔體流動速率 | 10 | g/10min | ASTM D-1238 |
| 熱變形溫度 | ASTM D-256 | ||
| 158 | ℃ | ||
| 110 | ℃ | ||
| 熔點 (10℃/min) | 165 | ℃ | DSC Method |
| 成型收縮率 (t3mm,直徑100mm) | 2.0 | % |