| 比重 | 1.41 | g/cm3 | ASTM D792 |
| 熔體質量流動速率 | 27 | g/10 min | ASTM D1238 |
| 成型收縮率 (flow,3.00MM) | 2.0 | % | ASTM D955 |
| 吸水率 (E,23℃,60%rh) | 0.22 | % | ASTM D570 |
| 洛氏硬度 (M-Scale) | 80 | ASTM D785 |
| 拉伸強度 (Yield,23℃) | 62.0 | MPa | ASTM D638 |
| 拉伸伸長率 (Break,23℃) | 40 | % | ASTM D638 |
| 彎曲模量 (23°C) | 2650 | MPa | ASTM D790 |
| 彎曲強度 (23°C) | 91.0 | MPa | ASTM D790 |
| 剪切強度 (2.00mm) | 55.0 | MPa | ASTM D732 |
| IZOD缺口沖擊強度 (3.20mm) | 59.0 | J/m | ASTM D256 |
| 表面電阻率 | 1.0E+16 | ohms | ASTM D257 |
| 體積電阻率 | 1.0E+14 | ohm·cm | ASTM D257 |
| 電氣強度 | 19 | kV/mm | ASTM D149 |
| 介電常數 (1E+6 Hz) | 3.70 | ASTM D150 | |
| 介質損耗因數 (1E+6 Hz) | 0.0070 | ASTM D150 |
| 熱畸變溫度 | ASTM D648 | ||
| (0.45MPa,未退火) | 158 | °C | |
| 110 | °C | ||
| 熔融溫度 | 165 | °C | |
| 線性熱膨脹系數 (flow,20 to 80°C) | 0.00013 | cm/cm/°C | ASTM D696 |
| 阻燃等級 (0.8mm) | HB | UL 94 |