| 熔體流動速率 | 8.0 | g/10min | ASTM D-1238 |
| 密度 | 0.90 | g/cm | ASTM D-1505 |
| 成型收縮率 | 1.6-1.8 | % | HPC Method |
| 沖擊強度 | 3.5 | kg·cm/cm | ASTM D-256 |
| 終拉伸率 | >500 | % | ASTM D-638 |
| 洛氏硬度 | 95 | R | ASTM D-785 |
| 拉伸屈服強度 | 290 | Kg/cm | ASTM D-638 |
| 沖擊強度 | 8.0 | kg·cm/cm | ASTM D-256 |
| 彈性撓曲模量 | 16,000 | Kg/cm | ASTM D-790 |
| 熱變形溫度 | 120 | ℃ | ASTM D-648 |
| 耐熱性 (130℃老化) | >3,000 | hour | HPC Method |
| 維卡軟化點 | 145 | ℃ | ASTM D-1525 |