| 特性 | 光澤，低 |
| 用途 | 工業應用 |
| 加工方法 | 擠出 |
| 比重 | 1.07 | g/cm3 | ASTM D792 |
| 熔流率（熔體流動速率）(220°C/10.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| 收縮率 - 流動(3.20 mm) | 0.40 到 0.70 | % | ASTM D955 |
| 洛氏硬度(R級) | 81 | ASTM D785 |
| 抗張強度1(屈服, 3.20 mm) | 32.4 | MPa | ASTM D638 |
| 伸長率2(斷裂, 3.20 mm) | 65 | % | ASTM D638 |
| 彎曲模量3(6.40 mm) | 1520 | MPa | ASTM D790 |
| 彎曲強度4(屈服, 6.40 mm) | 49.0 | MPa | ASTM D790 |
| 懸壁梁缺口沖擊強度 | ASTM D256 | ||
| -30°C, 3.20 mm | 49 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 39 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 98 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 9.0 | J/m | ASTM D256 |
| 載荷下熱變形溫度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40mm5 | 85.0 | °C | ASTM D648 |
| 0.45 MPa, 未退火, 6.40mm6 | 79.0 | °C | ASTM D648 |
| 維卡軟化溫度 | 86.0 | °C | ASTM D15257 |
| 光澤度(45°) | 30 | ASTM D2457 |
| 干燥溫度 | 70.0 到 80.0 | °C | |
| 干燥時間 | 3.0 到 4.0 | hr | |
| 建議的大水分含量 | < 0.010 | % | |
| 料筒1區溫度 | 180 到 210 | °C | |
| 料筒2區溫度 | 190 到 230 | °C | |
| 料筒3區溫度 | 200 到 250 | °C | |
| 料筒4區溫度 | 200 到 250 | °C | |
| 接頭溫度 | 200 到 250 | °C | |
| 熔體溫度 | 200 到 250 | °C | |
| 口模溫度 | 200 到 250 | °C |