| 熔體流動速率 | ASTM D-1238 | ||
| (200℃/5kg) | 5.5 | g/10min | |
| (230℃/3.8kg) | 10.0 | g/10min | |
| 吸水率 (24hr) | 0.3 | % | ASTM D-570 |
| 比重 | 1.07 | g/cm | ASTM D-792 |
| 模具收縮率 (Flow) | 0.2-0.6 | % | ASTM D-955 |
| 拉伸強度 | 620 | kg/cm | ASTM D-638 |
| 斷裂伸長率 | 4.5 | % | ASTM D-638 |
| 彎曲模量 | 33600 | kg/cm | ASTM D-790 |
| 彎曲強度 | 900 | kg/cm | ASTM D-790 |
| IZOD缺口沖擊強度 (3.2mm) | 1.5 | J/m | ASTM D-256 |
| 洛氏硬度 | 82 | M scale | ASTM D-785 |
| 熱變形溫度 (18.6kg/cm.未退火) | 90 | ℃ | ASTM D-648 |
| 維卡軟化溫度 (1kg,50℃/h) | 107 | ℃ | ASTM D-1525 |
| 燃燒性 (1.6mm) | HB | UL 94 |