| 比重 | 1.04 | 23/23℃ | ASTM D-792 |
| 熔體流動速率 | ASTM D-1238 | ||
| (220℃×10kg) | 18 | g/10min | |
| (200℃×5kg) | 1.7 | g/10min | |
| 燃燒性 (File No. E56070 UL&C-UL) | 1/16"HB |
| 引張強度 | 6870 | lb/in | ASTM D-638 |
| 彎曲彈性率 | ASTM D-790 | ||
| 2.7×10 | kg/cm | ||
| 3.8×10 | lb/in | ||
| 洛氏硬度 | 110 | R | ASTM D-785 |
| IZOD沖擊強度 (1/4") | 23 | kg.cm/cm | ASTM D-256 |
| 彎曲強度 | 780 | kg/cm | ASTM D-790 |
| 伸長率 | 20 | % | ASTM D-638 |
| 引張強度 | 485 | kg/cm | ASTM D-638 |
| 彎曲強度 | 11000 | lb/in | ASTM D-790 |
| IZOD沖擊強度 | ASTM D-256 | ||
| (1/8") | 26 | kg.cm/cm | |
| (1/8") | 4.8 | ft.lb/in | |
| (1/4") | 4.2 | ft.lb/in |
| 熱變形溫度 | 99(210) | ℃ | ASTM D-648 |
| 維卡軟化點 | ASTM D-1525 | ||
| 105 | ℃ | ||
| 221 | ℉ | ||
| 熱變形溫度 | 88(190) | ℉ |