2.5mm進口MWA純鎳Ni99鑄鐵焊條Mac Cast E405

英國進口MWA鑄鐵焊條Mac Cast E405|ENi-CI|鑄造修復|鑄鐵冷熱焊接

Superior high quality fully machinable nickel electrode for joining and building up on cast irons. Builds up quickly and produces sound fully machinable deposits. Minimum base metal dilution. No undercut. For hot and cold welding of cast irons and for joining or building up on malleable iron, steels and copper or one to another. Ideal for foundry reclamation. Also available as a TIG and MIG wire.

品質卓越、可完全加工的Ni99純鎳鑄鐵焊條，用于鑄鐵的連接和堆焊。迅速形成并產生良好的完全可加工的熔覆層。最小母材稀釋。沒有咬邊。用于鑄鐵的冷熱焊接，以及可鍛鑄鐵、鋼和銅或之間的連接或堆焊，是用于鑄造修復的理想選擇。有對應TIG/MIG焊絲可供選擇。

典型應用：發(fā)動機缸體、缸蓋、泵殼、齒輪箱殼體、泵閥座以及機器底座的斷裂和裂紋修復；當要求焊后高可加工性時填充孔洞和對磨損或缺失部分堆焊的理想選擇，比如鑄造缺陷的修復。

Typical All Weld Metal Chemical Analysis (%)

典型全焊縫金屬成分

Typical All Weld Metal Mechanical Properties（As Welded）

典型全焊縫金屬機械性能（焊態(tài)）：

Tensile Strength抗拉強度：       340 N/mm²

Elongation延伸率：                  15%

Hardness硬度：                     170 HB

Sizes Available and Recommended Amperages

尺寸Φ/電流：

Current電流：AC/DC (+)

Related Specification參考標準：AWS A5.15 ENi-CI

Storage儲存：Electrodes should be stored in dry conditions. Should the electrodes become damp, re-dry for one hour at 150°C before use. 焊條應儲存在干燥環(huán)境中。如果焊條受潮，應在150°C下重新干燥1小時后再使用。

使用E405鑄鐵焊條冷焊修復之優(yōu)越性：

1）在大多數(shù)情況下，不需要預熱或焊后熱處理。因此大大簡化了焊接工藝過程，并大大改善焊工的勞動條件。

2）對防止或減少工件變形十分有利。

3）工件無論大小都能適合焊接。

4）焊條可進行全方位焊接，無需要把焊件從機器上拆卸下來（現(xiàn)場）

使用注意事項：

如有可能，清潔焊接區(qū)域。去除表皮和所有銳邊。確保施焊部位沒有油污等。

推薦采用“U”坡口接頭。

使用3mm鉆頭在裂縫末端鉆孔，以防止焊接過程中進一步擴展。

從裂縫的末端開始焊接，向內焊接。

使用低電流并保持短弧。

應使用短線狀焊道(2-3cm)或窄編織焊道，以防止過熱。

采用直流焊機時根據(jù)熔敷情況改變正負極。

斷開電弧時，始終填充弧坑，并將焊條拉回到焊縫熔敷層上。

趁熱錘擊將有助于降低收縮應力。

重新引弧時，電弧從先前沉積的焊縫金屬開始，而不是從母材開始。

讓零件慢慢冷卻。